| 品牌 | UMG |
| 貨號 | ABS |
| 用途 | 頭盔 |
| 特性級別 | 標準級|||耐老化|||高強度|||高光澤||| |
| 牌號 | EX47E |
| 型號 | EX47E |
| 加工級別 | |
| 品名 | ABS |
| 外形尺寸 | 顆粒 |
| 用途級別 | 通用級||| |
| 生產(chǎn)企業(yè) | UMG |
| 是否進口 | 是 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 燃燒性 | File No. E56070 UL&C-UL | 1/16"HB | ||
| 熔體流動速率 | 200℃×5kg | ASTM D-1238 | 1.1 | g/10min | |
| 熔體流動速率 | 220℃×10kg | ASTM D-1238 | 12 | g/10min | |
| 比重 | ASTM D-792 | 1.03 | 23/23℃ | ||
| 機械性能 | IZOD沖擊強度 | 1/4" | ASTM D-256 | 6.6 | ft.lb/in |
| IZOD沖擊強度 | 1/4" | ASTM D-256 | 36 | kg.cm/cm | |
| IZOD沖擊強度 | 1/8" | ASTM D-256 | 41 | kg.cm/cm | |
| 彎曲強度 | ASTM D-790 | 620 | kg/cm2 | ||
| 彎曲彈性率 | ASTM D-790 | 2.2×104 | kg/cm2 | ||
| 彎曲彈性率 | ASTM D-790 | 3.1×105 | lb/in2 | ||
| 彎曲強度 | ASTM D-790 | 8800 | lb/in2 | ||
| 洛氏硬度 | ASTM D-785 | 108 | R | ||
| 引張強度 | ASTM D-638 | 5470 | lb/in2 | ||
| IZOD沖擊強度 | 1/8" | ASTM D-256 | 7.5 | ft.lb/in | |
| 引張強度 | ASTM D-638 | 385 | kg/cm2 | ||
| 伸長率 | ASTM D-638 | 30 | % | ||
| 熱性能 | 熱變形溫度 | ASTM D-648 | 86(187) | ℉ | |
| 維卡軟化點 | ASTM D-1525 | 217 | ℉ | ||
| 維卡軟化點 | ASTM D-1525 | 103 | ℃ | ||
| 熱變形溫度 | ASTM D-648 | 97(206) | ℃ | ||
顆粒和包裝圖片：
部分產(chǎn)品實例：
成型注意事項：
塑料ABS也可以說是聚苯乙烯的改性，比HIPS有較高的抗沖擊強度和更好的機械強度，具有良好的加工性能，可以使用注塑機、擠出機等塑料成型設備進行注塑、擠塑、吹塑、壓延、層合、發(fā)泡、熱成型，還可以焊接、涂覆、電鍍和機械加工。ABS的吸水性比較高，加工前需進行干燥處理，干燥溫度為70~85℃，干燥時間為2~6h；ABS制品在加工中容易產(chǎn)生內(nèi)應力，如應力太大，致使產(chǎn)品開裂，應進行退火處理，把制件放于70~80℃的熱風循環(huán)干燥箱內(nèi)2~4h，再冷卻至室溫即可。