產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 密度 | ASTM D-792 |
|
1.42 |
|
| 物理性能 | 吸水量 | 浸泡均衡點(diǎn)+73℉(+23℃) | ASTM D-570 | 1.40 | % |
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D-570 | 0.32 | % | |
| 機(jī)械性能 | 彎曲疲勞忍耐限度 | +73℉ | ASTM D-671 | 4.0 | MPsi |
| 擴(kuò)散因數(shù) | +73℉(+23℃)106Hz | ASTM D-150 | 0.005 |
|
|
| 伸張強(qiáng)度 | +250℉ | ASTM D-638 | 3.3 | MPsi | |
| 斷裂時(shí)之拉力伸張度 | +250℉(+122℃) | ASTM D-638 | >260 | % | |
| 伸張強(qiáng)度 | +122℃ | ASTM D-638 | 22.8 | MPa | |
| 彎曲疲勞忍耐限度 | +23℃ | ASTM D-671 | 27.6 | MPa | |
| 壓縮應(yīng)力 | +73℉@1%Def. | ASTM D-695 | 4.5 | MPsi | |
| 伸張強(qiáng)度 | +158℉ | ASTM D-638 | 6.6 | MPsi | |
| 壓縮應(yīng)力 | +23℃@10%Def. | ASTM D-695 | 108 | MPa | |
| 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D-570 | 0.28 | % | |
| 彎曲降服強(qiáng)度 | +73℉ | ASTM D-790 | 13.6 | MPsi | |
| 撓曲系數(shù) | +73℉ | 在25℃下 | 400 | MPsi | |
| IZOD沖擊強(qiáng)度 | +23℃ | ASTM D-256 | 69.4 | j/m | |
| 伸張強(qiáng)度 | +70℃ | ASTM D-638 | 45.5 | MPa | |
| IZOD沖擊強(qiáng)度 | 40℃ | ASTM D-256 | 53.4 | j/m | |
| 伸張強(qiáng)度 | +23℃ | ASTM D-638 | 66.9 | MPa | |
| 伸張強(qiáng)度 | +212℉ | ASTM D-638 | 4.3 | MPsi | |
| 彈性系數(shù) | +23℃ | ASTM D-638 | 3100 | MPa | |
| 撓曲系數(shù) | +212℉ | 在25℃下 | 130 | MPsi | |
| 伸張強(qiáng)度 | +73℉ | ASTM D-638 | 9.7 | MPsi | |
| 撓曲系數(shù) | +23℃ | 在25℃下 | 2760 | MPa | |
| 伸張強(qiáng)度 | -68℉ | ASTM D-638 | 14.0 | MPsi | |
| 斷裂時(shí)之拉力伸張度 | +212℉(+100℃) | ASTM D-638 | >260 | % | |
| 彈性系數(shù) | +73℉ | ASTM D-638 | 450 | MPsi | |
| 伸張強(qiáng)度 | -55℃ | ASTM D-638 | 96.5 | MPa | |
| 剪力 | +23℃ | ASTM D-732 | 65.5 | MPa | |
| 撓曲系數(shù) | +70℃ | 在25℃下 | 1515 | MPa | |
| 伸張強(qiáng)度 | +100℃ | ASTM D-638 | 29.6 | MPa | |
| 撓曲系數(shù) | +158℉ | 在25℃下 | 220 | MPsi | |
| 斷裂時(shí)之拉力伸張度 | +73℉(+23℃) | ASTM D-638 | 25 | % | |
| 撓曲系數(shù) | -55℃ | 在25℃下 | 3930 | MPa | |
| 壓縮應(yīng)力 | +73℉@10%Def. | ASTM D-695 | 15.6 | MPsi | |
| 撓曲系數(shù) | -68℉ | 在25℃下 | 570 | MPsi | |
| 壓縮應(yīng)力 | +23℃@1%Def. | ASTM D-695 | 31.0 | MPa | |
| 摩擦系數(shù) | +73℉(+23℃)動(dòng)態(tài) | ThrustWasherTest3 | 0.20 |
|
|
| 負(fù)載下之變形 | 2000psi@+122℉(14Mpa@50℃) | ASTM D-621 | 0.7 | % | |
| 剪力 | +73℉ | ASTM D-732 | 9.5 | MPsi | |
| IZOD沖擊強(qiáng)度 | -40℉ | ASTM D-256 | 1.0 | ft.lb/in | |
| 彎曲降服強(qiáng)度 | +23℃ | ASTM D-790 | 93.8 | MPa | |
| 撓曲系數(shù) | +100℃ | 在25℃下 | 895 | MPa | |
| 撓曲系數(shù) | +122℃ | 在25℃下 | 550 | MPa | |
| 斷裂時(shí)之拉力伸張度 | +158℉(+70℃) | ASTM D-638 | 150 | % | |
| IZOD沖擊強(qiáng)度 | +73℉ | ASTM D-256 | 1.3 | ft.lb/in | |
| 電氣性能 | 絕緣強(qiáng)度 | Short Time,2.3mm | ASTM D-149 | 19.7 | MV/m |
| 電阻系數(shù) | +73℉(+23℃)0.2%H2O | ASTM D-257 | 1015 | ohm-cm | |
| 絕緣系數(shù) | +73℉(+23℃)102to106Hz | ASTM D-150 | 3.7 |
|
|
| 電弧 | 120mil(3.1mm) | ASTM D-495 | 220no tracking | Sec. | |
| 絕緣強(qiáng)度 | Short Time,90 mils | ASTM D-149 | 500 | V/mil | |
| 熱性能 | 線性熱膨脹系數(shù) | +220 to +300℉ | ASTM D-696 | 8.3 | 10-5in/in.℉ |
| 線性熱膨脹系數(shù) | +140 to +220℉ | ASTM D-696 | 7.6 | 10-5in/in.℉ | |
| 熱變形溫度 | 0.5MPa | ASTM D-648 | 170 | ℃ | |
| 熱變形溫度 | 1.8MPa | ASTM D-648 | 130 | ℃ | |
| 線性熱膨脹系數(shù) | +60 to +104℃ | ASTM D-696 | 13.7 | 10-5m/m.℃ | |
| 熔點(diǎn) |
|
ASTM D-2133 | 347 | ℉ | |
| 線性熱膨脹系數(shù) | +29 to +60℃ | ASTM D-696 | 12.2 | 10-5m/m.℃ | |
| 線性熱膨脹系數(shù) | -40 to +85℉ | ASTM D-696 | 5.8 | 10-5in/in.℉ | |
| 可燃燒性 |
|
UL-94 | 94HB |
|
|
| 熔點(diǎn) | ASTM D-2133 |
|
175 | ℃ | |
| 熱變形溫度 | 66psi | ASTM D-648 | 328 | ℉ | |
| 線性熱膨脹系數(shù) | +104 to +150℃ | ASTM D-696 | 14.9 | 10-5m/m.℃ | |
| 線性熱膨脹系數(shù) | -40 to +29℃ | ASTM D-696 | 10.4 | 10-5m/m.℃ | |
| 熱變形溫度 | 264psi | ASTM D-648 | 266 | ℉ | |
| 線性熱膨脹系數(shù) | +85 to +140℉ | ASTM D-696 | 6.8 | 10-5in/in.℉ | |
（1） POM加工前可不用干燥,*在加工過(guò)程中進(jìn)行預(yù)熱(80℃左右),對(duì)產(chǎn)品尺寸的穩(wěn)定性有好處.
（2） POM的加工溫度很窄(0～215℃),在炮筒內(nèi)停留時(shí)間稍長(zhǎng)或溫度超過(guò)220℃時(shí)就會(huì)分解,產(chǎn)生刺激性強(qiáng)的甲醛氣體.
（3） POM料注塑時(shí)保壓壓力要較大(與注射壓力相近),以減少壓力降.螺桿轉(zhuǎn)速不能過(guò)高,殘量要少;
（4） POM產(chǎn)品收縮率較大,易產(chǎn)生縮水或變形.POM比熱大,模溫高(80～100℃),產(chǎn)品脫模時(shí)很燙,需防止手指.
（5） POM宜在“中壓、中速、低料溫、較高模溫”的條件下成型加工,精密制品成型時(shí)需用控制模溫
（6） 具高機(jī)械強(qiáng)度和剛性
（7） *的疲勞強(qiáng)度
（8） 環(huán)境抵抗性、耐有機(jī)溶劑性佳
（9） 耐反覆沖擊性強(qiáng),良好的電氣性質(zhì),復(fù)原性良好,具自已潤(rùn)滑性、耐磨性良好,尺寸安定性優(yōu)庫(kù)存圖片